Data for PERIDOT SLS Duraform Material
The Selective Laser Sintering (SLS) process creates solid, three dimensional objects by fusing powdered materials with a CO2 laser. Once the 3D CAD data is sliced in the software and downloaded, the SLS process can begin. As the process begins, a layer of heat-fusible powder is deposited across the part build chamber. An initial cross-section of the object under fabrication is selectively 'drawn' on the layer of powder by a heat generating CO2 laser. The interaction of the laser beam with the powder fuses the powder particles to form a solid mass. An additional layer of powder is deposited via a roller mechanism on top of the previously scanned layer. The process is repeated, with each layer fusing to the layer below it until the part is complete.
|
Units |
Test Method |
DuraForm |
||
Mechanical |
|||||
Tensile Strength |
|
ASTM |
|
||
Tensile Modulus |
|
ASTM |
|
||
Tensile Elongation at Break |
% |
ASTM |
9 |
||
Flexural Modulus |
|
ASTM |
|
||
Stress at 5% Strain |
|
ASTM |
— |
||
Stress at 10% Strain |
|
ASTM |
— |
||
Impact Strength |
|||||
Notched Izod |
|
ASTM |
|
||
Unnotched Izod |
|
ASTM |
|
||
Initial Tear Resist. Die C at 73° F |
|
ASTM |
— |
||
Abrasion Resist. |
mg/1000 cycles |
ASTM |
— |
||
Hardness |
Shore A |
ASTM |
— |
||
Thermal |
|||||
Melting Point: T m |
|
DSC |
|
||
DTUL, 66 psi |
|
ASTM |
|
||
DTUL, 264 psi |
|
ASTM |
|
||
Electrical |
|||||
Volume Resistivity |
(Ohm X cm) |
ASTM |
3.1 x 1014 |
||
Surface Resistivity |
(Ohm X cm) |
ASTM |
|
||
Dielectric Constant |
|
ASTM |
2.9 |
||
Dielectric Strength 22 C, 50% RH, in air, 500V/sec |
(v/mm) |
ASTM |
1.6 x 104 |
||
Other |
|||||
Surface Finish (upper facing, no post) |
|
— |
|
||
Surface Finish (upper facing, with post) |
|
— |
|
||